Toughness and R-curve behaviour of laminated Si3N4/SiCw ceramics

Laminated Si₃N₄/SiC_w ceramics were successfully prepared by tape casting and hot-pressing. Its mechanical properties were measured and the impact resistance was discussed. The toughness of the laminated Si₃N₄/SiC_w ceramics was 13.5 MPa m^1/2, which was almost 1.6 times that of Si₃N₄/SiC_w composite ceramics, namely 8.5 MPa m^1/2. Moreover, the indentation strength of laminated Si₃N₄/SiC_w ceramics was not sensitive to increasing indentation loads and exhibited a rising R-curve behaviour, indicating that the laminated Si₃N₄/SiC_w ceramics had excellent impact resistance. The improved toughness and impact resistance of laminated Si₃N₄/SiC_w ceramics was attributed to the residual stress caused by a thermal expansion coefficient mismatch between the different layers, resulting in crack deflection and bridging of SiC whiskers in the interface layer, thus consuming a large amount of fracture work.     

Nacre-Inspired,Liquid Metal-Based Ultrasensitive Electronic Skin by Spatially Regulated Cracking Strategy

The realization of liquid metal-based wearable systems will be a milestone toward high-performance, integrated electronic skin. However, despite the revolutionary progress achieved in many other components of electronic skin, liquid metal-based flexible sensors still suffer from poor sensitivity due to the insufficient resistance change of liquid metal to deformation. Herein, a nacre-inspired architecture composed of a biphasic pattern (liquid metal with Cr/Cu underlayer) as “bricks” and strain-sensitive Ag film as “mortar” is developed, which breaks the long-standing sensitivity bottleneck of liquid metal-based electronic skin. With 2 orders of magnitude of sensitivity amplification while maintaining wide (>85%) working range, for the first time, liquid metal-based strain sensors rival the state-of-art counterparts. This liquid metal composite features spatially regulated cracking behavior. On the one hand, hard Cr cells locally modulate the strain distribution, which avoids premature cut-through cracks and prolongs the defect propagation in the adjacent Ag film. On the other hand, the separated liquid metal cells prevent unfavorable continuous liquid-metal paths and create crack-free regions during strain. Demonstrated in diverse scenarios, the proposed design concept may spark more applications of ultrasensitive liquid metal-based electronic skins, and reveals a pathway for sensor development via crack engineering.     

Synthesis of nanopowders with low agglomeration by elaborating Φ values for producing Gd2O3-MgO nanocomposites with extremely fine grain sizes and high mid-infrared transparency

Refining ceramic microstructures to the nanometric range to minimize light scattering provides an interesting methodology for developing novel optical ceramic materials. In this work, we reported the fabrication and properties of a new nanocomposite optical ceramic of Gd₂O₃-MgO. The citric acid sol-gel combustion method was adopted to fabricate Gd₂O₃-MgO nanocomposites with fine-grain sizes, dense microstructures and homogeneous phase domains. Nanopowders with low agglomeration and improved sinterability can be obtained by elaborating Φ values. Further refining of the microstructure of the nanocomposites was achieved by elaborating the hot-pressing conditions. The sample sintered at 65 MPa and 1300 °C showed a quite high hardness value of 14.3 ± 0.2 GPa, a high transmittance of 80.3 %–84.7 % over the 3?6 μm wavelength range, due mainly to its extremely fine-grain size of Gd₂O₃ and MgO (93 and 78 nm, respectively) and high density.     

有机二氟化硼配合物的合成及压致变色性能表征

以阿伏苯宗和三氟化硼为原料,经过一步反应,合成阿伏苯宗二氟化硼(BF2AVB),产物的结构经1HNMR谱确证.基于荧光光谱与X射线粉末衍射测试,对BF2AVB的压致发光性能和机理进行研究.本实验原料易得,反应条件温和,实验操作简单,反应收率高.BF2AVB的压致变色现象明显,通过探讨压致变色机理,加深同学对压致变色材料的了解.同时,该实验可以拓展学科知识,激发学生的专业热情和科研兴趣.     

Enhanced electromagnetic microwave absorption of Fe/C/SiCN composite ceramics targeting in integrated structure and function

The Fe/C/SiCN composite ceramics were synthesized by polymer-derived method to obtain the integration of structure and functions. The electromagnetic waves (EMW) absorption properties at X and Ku bands were investigated. The addition of nano-sized Fe particles improved the magnetic loss and impedance matching, and the carbon nanotubes generated by the iron in-situ catalysis increased the internal relaxation polarization and interfacial polarization, which together improved the EMW absorption properties significantly. In particular, the Fe/C/SiCN-9 showed the optimum reflection loss (RL) of ?31.06 dB at 10.03 GHz with an effective absorption bandwidth (EAB, RL < ?10 dB) of 3.03 GHz at 2.51 mm, indicating the excellent EMW absorption properties of Fe/C/SiCN composite ceramics.     

Multiple clusterings of heterogeneous information networks

Machine Learning - Traditional clustering algorithms focus on a single clustering result; as such, they cannot explore potential diverse patterns of complex real world data. To deal with this...     

Auto-registration of medium and high spatial resolution satellite images by integrating improved SIFT and spatial consistency constraints

Feature-based methods have been developed in the past decades for the registration of optical satellite images. However, it is still a challenging problem to handle well the registration between medium and high spatial resolution images due to the large difference of the spatial structural features and local details for the same objects. In this study, an automated co-registration technique is proposed that integrates an improved SIFT (I-SIFT) and a novel matching strategy called spatial consistency constraints (SCC) to cope with the large difference in spatial resolutions between the image pair. Three constraints on angle, distance, and ratio are introduced to re the initial matching features obtained by I-SIFT. Three groups of experiments were conducted to validate the effectiveness of the proposed method. The experiments used high resolution multispectral and panoramic SPOT 5/6 images and Landsat 5/8 orthorectification images. Experimental results show that the registration error lies in about 1 pixel of high-resolution images and demonstrate that the proposed I-SIFT-SCC approach is suitable for fine registration of optical satellite images from medium spatial resolution to high spatial resolution with resolution ratio up to 6.